Effects of synthesis conditions on structure and magnetic properties of MnFe2O4 particles
Manganese ferrite (MnFe2O4) nanoparticles were synthesized through a coprecipitation method using manganese (II) chloride tetrahydrate (MnCl2·4H2O) and ferric chloride hexahydrate (FeCl3·6H2O) as precursors. The scanning electron microscopy images showed that the as-synthesized particles were granul...
Lưu vào:
| Tác giả chính: | , , , , , , |
|---|---|
| Định dạng: | Bài Báo |
| Ngôn ngữ: | Vietnamese |
| Nhà xuất bản: |
ICE Publishing
2020
|
| Chủ đề: | |
| Truy cập trực tuyến: | https://www.icevirtuallibrary.com/doi/abs/10.1680/jgrma.20.00010 https://dlib.phenikaa-uni.edu.vn/handle/PNK/580 |
| Từ khóa: |
Thêm từ khóa
Không có từ khóa, Hãy là người đầu tiên đánh dấu biểu ghi này!
|
| Tóm tắt: | Manganese ferrite (MnFe2O4) nanoparticles were synthesized through a coprecipitation method using manganese (II) chloride tetrahydrate (MnCl2·4H2O) and ferric chloride hexahydrate (FeCl3·6H2O) as precursors. The scanning electron microscopy images showed that the as-synthesized particles were granular and about 20 nm. The X-ray diffraction patterns revealed that the manganese ferrite phase was completely decomposed into ferric oxide (Fe2O3) and manganese (III) oxide (Mn2O3) after annealing above 800°C in air. In contrast, its crystalline quality significantly improved when it was annealed in argon. By using the vibrating-sample magnetometry technique, it was demonstrated that the saturation magnetization (M s) of the as-prepared sample (∼36.6 emu/g) decreased sharply up to ∼5 emu/g after annealing at 1000°C in air and significantly increased to ∼77.6 emu/g when it was annealed at 1000°C in argon. Under sunlight radiation, a higher efficiency was observed for manganese ferrite particles annealed in argon in the presence of hydrogen peroxide (H2O2), mainly due to the Fenton reaction between manganese ferrite and hydrogen peroxide. The authors suggest that the presence of hydrogen peroxide and the enhancement of the crystalline quality of the manganese ferrite phase are the two leading factors in improving methylene blue degradation efficiency. |
|---|