Low driving field-induced large strain in ternary lead-free Na0.5Bi0.5TiO3-SrTiO3-ABO3 piezoceramics
In this letter, three ternary lead-free Na0.5Bi0.5TiO3-SrTiO3-ABO3 piezoceramics (ABO3 = LiNbO3, BaZrO3, and LaFeO3) were studied. The addition of ABO3 into Na0.5Bi0.5TiO3-SrTiO3 ceramic induces a ferroelectric tetragonal-to-ergodic relaxor pseudocubic phase transition, resulting in the significant...
Lưu vào:
| Tác giả chính: | , |
|---|---|
| Định dạng: | Bài trích |
| Ngôn ngữ: | English |
| Nhà xuất bản: |
Elsevier
2022
|
| Chủ đề: | |
| Truy cập trực tuyến: | https://www.sciencedirect.com/science/article/abs/pii/S0167577X22001252?via%3Dihub https://dlib.phenikaa-uni.edu.vn/handle/PNK/5730 https://doi.org/10.1016/j.matlet.2022.131772 |
| Từ khóa: |
Thêm từ khóa
Không có từ khóa, Hãy là người đầu tiên đánh dấu biểu ghi này!
|
| Tóm tắt: | In this letter, three ternary lead-free Na0.5Bi0.5TiO3-SrTiO3-ABO3 piezoceramics (ABO3 = LiNbO3, BaZrO3, and LaFeO3) were studied. The addition of ABO3 into Na0.5Bi0.5TiO3-SrTiO3 ceramic induces a ferroelectric tetragonal-to-ergodic relaxor pseudocubic phase transition, resulting in the significant disruption of ferroelectric order with the shift of the ferroelectric-relaxor transition temperature down to below room temperature. The conventional furnace sintering and microwave sintering methods are conducted in this study to improve the electric field-induced strain properties of BNST-LN piezoceramic. Interestingly, the Na0.5Bi0.5TiO3-SrTiO3-LiNbO3 sample sintered via microwave sintering method shows an ultrahigh normalized strain of 995 pm/V at an ultralow driving field of 2 kV/mm, suggesting a potential candidate for lead-free piezoactuator applications. |
|---|