Stress Corrosion Cracking Behavior in API 5L Steels for Sour Service

This work presents a study on the behavior of stress corrosion cracking (SCC) phenomenon in pipeline steels for sour service in near-neutral media. SCC tests under static stressing conditions were performed in planar steel samples using a Cortest proof-ring coupled with a fabricated cell containing...

Mô tả chi tiết

Lưu vào:
Hiển thị chi tiết
Tác giả chính: Blanco, A., Hallen, J. M., Tu, Manh Le
Định dạng: Bài trích
Ngôn ngữ:English
Nhà xuất bản: Springer 2022
Chủ đề:
Pipeline steel
Stress corrosion cracking
Truy cập trực tuyến:https://link.springer.com/chapter/10.1007/978-3-030-92574-1_87
https://dlib.phenikaa-uni.edu.vn/handle/PNK/5719
https://doi.org/10.1007/978-3-030-92574-1_87
Từ khóa: Thêm từ khóa
Không có từ khóa, Hãy là người đầu tiên đánh dấu biểu ghi này!
id oai:localhost:PNK-5719
record_format dspace
spelling oai:localhost:PNK-57192022-08-17T05:54:50Z Stress Corrosion Cracking Behavior in API 5L Steels for Sour Service Blanco, A. Hallen, J. M. Tu, Manh Le Pipeline steel Stress corrosion cracking This work presents a study on the behavior of stress corrosion cracking (SCC) phenomenon in pipeline steels for sour service in near-neutral media. SCC tests under static stressing conditions were performed in planar steel samples using a Cortest proof-ring coupled with a fabricated cell containing near-neutral pH solution as a corrosive medium, which simulates the soil conditions, to observe the cracking initiation stage. Characterizations of the steel samples using surface techniques such as SEM, EDS, and Raman spectroscopy show that the presence of nonmetallic inclusions takes place as pitting sites (to form corrosion pits), which constitute the most susceptible sites for SCC crack initiation. SEM images taken on the steel sample surfaces exhibit both SCC transgranular and intergranular crack types in near-neutral media. Although the obtained results are interesting, further study is necessary to evaluate and confirm the role of inclusions in SCC initiation mechanisms. 2022-05-05T07:26:11Z 2022-05-05T07:26:11Z 2022 Bài trích https://link.springer.com/chapter/10.1007/978-3-030-92574-1_87 https://dlib.phenikaa-uni.edu.vn/handle/PNK/5719 https://doi.org/10.1007/978-3-030-92574-1_87 en Springer
institution Digital Phenikaa
collection Digital Phenikaa
language English
topic Pipeline steel
Stress corrosion cracking
spellingShingle Pipeline steel
Stress corrosion cracking
Blanco, A.
Hallen, J. M.
Tu, Manh Le
Stress Corrosion Cracking Behavior in API 5L Steels for Sour Service
description This work presents a study on the behavior of stress corrosion cracking (SCC) phenomenon in pipeline steels for sour service in near-neutral media. SCC tests under static stressing conditions were performed in planar steel samples using a Cortest proof-ring coupled with a fabricated cell containing near-neutral pH solution as a corrosive medium, which simulates the soil conditions, to observe the cracking initiation stage. Characterizations of the steel samples using surface techniques such as SEM, EDS, and Raman spectroscopy show that the presence of nonmetallic inclusions takes place as pitting sites (to form corrosion pits), which constitute the most susceptible sites for SCC crack initiation. SEM images taken on the steel sample surfaces exhibit both SCC transgranular and intergranular crack types in near-neutral media. Although the obtained results are interesting, further study is necessary to evaluate and confirm the role of inclusions in SCC initiation mechanisms.
format Bài trích
author Blanco, A.
Hallen, J. M.
Tu, Manh Le
author_facet Blanco, A.
Hallen, J. M.
Tu, Manh Le
author_sort Blanco, A.
title Stress Corrosion Cracking Behavior in API 5L Steels for Sour Service
title_short Stress Corrosion Cracking Behavior in API 5L Steels for Sour Service
title_full Stress Corrosion Cracking Behavior in API 5L Steels for Sour Service
title_fullStr Stress Corrosion Cracking Behavior in API 5L Steels for Sour Service
title_full_unstemmed Stress Corrosion Cracking Behavior in API 5L Steels for Sour Service
title_sort stress corrosion cracking behavior in api 5l steels for sour service
publisher Springer
publishDate 2022
url https://link.springer.com/chapter/10.1007/978-3-030-92574-1_87
https://dlib.phenikaa-uni.edu.vn/handle/PNK/5719
https://doi.org/10.1007/978-3-030-92574-1_87
_version_ 1751856279361421312
score 8.891145

Tài liệu tương tự